Flurine® High Fluorine content H series Fluoroelastomer FKM

group name: Fluoroelastomer FKM

Min Order: 1 kilogram

brand name: Zheflon PVDF & Flurine FKM Manufacturer

model: H228,H728

Nearest port for product export: Ningbo, Shanghai

Delivery clauses under the trade mode: FOB, CFR, CIF, EXW, Express Delivery

Acceptable payment methods: T/T, L/C

update time: Tue, 28 Jan 2025 10:02:59 GMT

contact supplier

Paramtents

Features High fluorine content. High fluidity
Uses Shaft seals, oil seals, fuel hose. Extrusion moldi
Forms White or light-yellow flake

Packging & Delivery

Min Order1 kilogram

Briefing

Used in automotive, hydraulic, electrical and chemical industries.

Detailed

Description

Flurine® H series is a low and middle Mooney bisphenol-vulcanized fluoroelastomer with a fluorine content of 69%.

It is a copolymer of vinylidene fluoride (VF2) and hexafluoropropylene (HFP). It is commonly used in automotive, hydraulic, electrical and chemical industries.

It has excellent extrusion processability, excellent chemical resistance, low expansion rate, low fuel permeability, especially for fuel hoses.

Technical Specifications

General
Features	High fluorine content. High fluidity
Uses	Shaft seals, oil seals, fuel hose. Extrusion molding
Forms	White or light-yellow flake
Items	Typical Value		Test Method
Items	H228	H728	Test Method
Physical Properties
Fluorine Content（mass%）	69	69
Density（g/cc）	1.85~1.90	1.85~1.90	ASTM D297
Mooney Viscosity	20~49	50~99	ASTM D1646 ML 1+10 at 121°C
Water content	0.15	0.15	ASTM D 5668
Vulcanization Properties
T10（s）	<260	<120	ASTM D5289
T90（s）	<420	<360	ASTM D5289
Mechanical Properties
Tensile strength（MPa）	11	11	ASTM D412 Method A
100% Modulus	4.2	4.4	ASTM D412 Method A
Elongation at Break（%）	160	160	ASTM D412 Method A
Tearing Strength（KN/m）	15	18	ASTM D624
Hardness, Shore A	77	77	ASTM D2240, Type A
Compression Set	35	35	ASTM D395, Test B 70 hours at 200℃
Thermal Properties
TR10（℃）	-17	-17	ASTM D1329
Brittleness Temperature（℃）	-30	-30	ASTM D2137
Chemical resistance Properties
Resistance to liquids			Methanol, 23℃×70h
Tensile strength change rate（%）	-10	-8	ASTM D412 Method A
Elongation at Break change rate(%)	20	18	ASTM D412 Method A
100％Elongation change rate（%）	-12	-10	ASTM D412 Method A
Hardness change, Shore A	-4	-3	ASTM D2240, Type A
Volume change rate（%）	3.5	3.3
Formulation		Curing condition
Polymer 100 MT carbon black，N990 30		Press		Oven
Calcium hydroxide 6 Magnesium oxide 3		10min at 177°C,0.5°		24h at 230°C
Fluorocure-5# 2.5		10min at 177°C,0.5°		24h at 230°C

Process Safety Instructions

1）Store and use all fluoroelastomers only in a well-ventilated area.

2）Do not smoke in areas contaminated with dust from fluoroelastomers.

3）Avoid eye contact. After handling fluoroelastomers wash any skin that came in contact with the product with soap and water.

4）Potential hazards, including evolution of toxic vapors, exist during compounding or processing under high temperatures.

5）Before processing the fluoroelastomers, read and consult the MSDS, and follow all label directions and operation cautions..

Packaging And Storage

1）Fluoroelastomers be packed in PVC bags in the shape of rubber film, each bag weight 5KGS, and finally be put into a carton. Each carton contains 5 bags with net weight 25KGS.

2）It must be stored in a clean, cool, and dry place. The storage life is one year from the date of production. It must be re-inspected if over one year and only can use if qualified.

3）It is transported as non-dangerous chemicals. Avoid excessive vibration and far away from pollution, sunshine and water during the transport.