Flurine® Low Temperature Fluoroelastomer FKM

group name: Fluoroelastomer FKM

Min Order: 1 kilogram

brand name: Zheflon PVDF & Flurine FKM Manufacturer

model: L228,L728,L228A,L728A

Nearest port for product export: Ningbo, Shanghai

Delivery clauses under the trade mode: FOB, CFR, CIF, EXW, Express Delivery

Acceptable payment methods: T/T, L/C

update time: Thu, 21 Nov 2024 16:52:48 GMT

contact supplier

Paramtents

Features Low temperature resistance
Uses Shaft seal, O-ring, fuel pipe. Extrusion molding
Forms White or light-yellow flake

Packging & Delivery

Min Order1 kilogram

Briefing

Used in automotive, hydraulic, electrical and chemical industries.

Detailed

Description

Flurine® L series is a low-middle Mooney bisphenol-vulcanized fluoroelastomer with a fluorine content of 66%.

It is a copolymer of vinylidene fluoride (VF2), hexafluoropropylene (HFP) and perfluoroalkyl vinyl ether (PMVE).

It is commonly used in automotive, hydraulic, electrical and chemical industries. It has excellent heat and chemical resistance.The outstanding performance is low-temperature elasticity, which are particularly suitable for O-ring seals for fuel injectors.

Technical Specifications

General
Features	Low temperature resistance
Uses	Shaft seal, O-ring, fuel pipe. Extrusion molding
Forms	White or light-yellow flake
Items	Typical Value				Test Method
Items	L228	L728	L228A	L728A	Test Method
Physical Properties
Fluorine Content（mass%）	65		65
Density（g/cc）	1.78~1.82		1.78~1.82		ASTM D297
Mooney Viscosity	20~49	50~89	20~49	50~89	ASTM D1646 ML 1+10 at 121°C
Water content（%）	0.15		0.15		ASTM D 5668
Vulcanization Properties
T10（s）	<130		<160		ASTM D5289
T90（s）	<240		<300		ASTM D5289
Mechanical Properties
Tensile strength（MPa）	13		13		ASTM D412 Method A
100% Modulus	6		6		ASTM D412 Method A
Elongation at Break（%）	180		180		ASTM D412 Method A
Tearing Strength（KN/m）	15		15		ASTM D624
Hardness, Shore A	75		75		ASTM D2240, Type A
Compression Set	16		16		ASTM D395, Test B 70 hours at 200℃
Thermal Properties
Low temperature retraction, TR10（℃）	-19		-21		GB/T 7758
Brittleness Temperature（℃）	-27		-34		GB/T 15256
Chemical resistance Properties
Resistance to liquids					Methanol,23℃×70h
Tensile strength change rate（%）	-10		-10		ASTM D412 Method A
Elongation at Break change rate(%)	-9		-9		ASTM D412 Method A
100％Elongation change rate（%）	-12		-12		ASTM D412 Method A
Hardness change, Shore A	-1		-1		ASTM D2240, Type A
Volume change rate（%）	2		2
Formulation			Curing condition
Polymer 100 MT carbon black，N990 30			Press			Oven
Calcium hydroxide 6 Magnesium oxide 3			10min at 177°C,0.5°			24h at 230°C
Fluorocure-5# 2.5			10min at 177°C,0.5°			24h at 230°C

Process Safety Instructions

1）Store and use all fluoroelastomers only in a well-ventilated area.

2）Do not smoke in areas contaminated with dust from fluoroelastomers.

3）Avoid eye contact. After handling fluoroelastomers wash any skin that came in contact with the product with soap and water.

4）Potential hazards, including evolution of toxic vapors, exist during compounding or processing under high temperatures.

5）Before processing the fluoroelastomers, read and consult the MSDS, and follow all label directions and operation cautions..

Packaging And Storage

1）Fluoroelastomers be packed in PVC bags in the shape of rubber film, each bag weight 5KGS, and finally be put into a carton. Each carton contains 5 bags with net weight 25KGS.

2）It must be stored in a clean, cool, and dry place. The storage life is one year from the date of production. It must be re-inspected if over one year and only can use if qualified.

3）It is transported as non-dangerous chemicals. Avoid excessive vibration and far away from pollution, sunshine and water during the transport.